Synthesis and luminescent properties of new conjugated polymers based on poly(p-phenylene vinylene)
Abstract
The "push-pull" electronically substituted polymers poly(2 (5) -bromo-5 (2) -n-hexyloxy-1,4-phenylene vinylene), poly(2 (5) -chloro-5 (2) -n-hexyloxy-1,4-phenylene vinylene) and poly(2 (5) -fluoro-5 (2) -n-hexyloxy-1,4-phenylene vinylene) were synthesized by a soluble precursor method and were used to fabricate light emitting diode (LED) devices. Thermal elimination of the polyether precursors gives final conjugated polymers as flexible red films. Precursor polymers can be spin-cast from solutions onto indium/tin oxide (ITO) pretreated quartz plates, then thermally converted to the final red polymers. Light emitting diode fabrication is then completed by the thin film vapor deposition of calcium, followed by aluminum. LED devices of the "push-pull" polymers give light emission in the 620-635 nm range. Two fluorinated polymers, poly(2-fluoro-1,4-phenylene vinylene) and poly(2,5-difluoro-1,4-phenylene vinylene) were investigated for their electroluminescent (EL) properties. LED's using these materials as emissive layers show substantial EL wavelength shifts (560 nm and 600 nm, respectively) relative to emission from unsubstituted poly(1,4-phenylene vinylene) (565 nm). These differences in EL emission can be attributed to the electronic effects of fluorine substitution. Synthetic strategies were developed for copolymeric materials based on poly(1,4-phenylene vinylene). The alternating block copolymer, poly (1,8-octanedioxy-2,6-dimethoxy-1,4-phenylene-1,2-ethenylene-1,4-phenylene-1,2-ethenylene-1,4-phenylene-1,2-ethenylene- 3,5-dimethoxy-1,4-phenylene) was synthesized by a modified Wittig polymerization utilizing trialkyl phosphonium salts. This resulted in a regiospecific trans-olefination reaction when compared to polymeric materials synthesized through the use of common triaryl-phosphonium salts. Harsh post-Wittig isomerization procedures using I$\sb2$ were bypassed as a result of the high trans-cis ratio of the final copolymer. It was fully characterized using the standard spectroscopic techniques as well as elemental analysis. Light-emitting single-layer diodes using the soluble, processible copolymer as the emitting layer gives green light with an electroluminescence maximum at 513 nm.
Subject Area
Polymers|Organic chemistry|Materials science